304 SAE AMS 5513H-2004 Stainless steel wire manufacturer

304 SAE AMS 5513H-2004 stainless steel wire is widely used in a variety of domestic and industrial applications. Because stainless steel has a corrosion resistance and processing properties, it is also commonly used in the manufacture of fasteners, food processing equipment and other occasions that require high corrosion resistance and good processing properties.

Material designation	304
Correspondence standard	SAE AMS 5513H-2004 Steel, Corrosion-Resistant, Sheet, Strip, and Plate 19Cr - 9.2Ni (SAE 30304) Solution Heat Treated
Sort out	Austenitic stainless steel
Property	Strength Corrosion resistance low temperature ductile forging
Tag	Austenitic stainless steel composition similar to UNS S30400
Instructions	304 is a typical low-carbon austenitic stainless steel, corresponding to the domestic grade 0Cr18Ni9, the grade is on the basis of 302 to further reduce the carbon content of the obtained, with good processing molding and oxidation resistance, oxidation acid (such as nitric acid) has a strong corrosion resistance, alkali solution and most organic acids and inorganic acids also have a certain corrosion resistance. It has good welding performance. Austenitic stainless steel cannot be strengthened by heat treatment and can only be strengthened by work hardening.
	304 Good cold processing performance, bolts, screws can be cold heading molding, other products can also be bent, crimping, folding, deep drawing and other processing, hot processing performance can also be.
	304 is widely used in standard parts, in addition to the production of national standard products, but also the production of some low-strength beacon products, a variety of enterprise standard products more production.
	Selection suggestions:
	Tensile strength of 500Mpa or 700Mpa above, with oxidation resistance, acid, alkali and salt corrosion resistance, while there is no magnetic requirements, recommended use.
Density	7.85g/cm3

304 SAE AMS 5513H-2004 Stainless steel wire manufacturer Stainless-steel-wire-manufacturer

304 SAE AMS 5513H-2004 stainless steel wire can be used under welding conditions and maintain its corrosion resistance, so it does not need to be annealed. However, in some specific cases, appropriate heat treatment may be required if further corrosion resistance or processability is required.

304 Chemical element content (%)

Ingredient	C	Si	Mn	P	S	Cr	Ni	Cu	Mo
Minimum value	-	-	-	-	-	18	8	-	-
Maximum value	0.08	1	2	0.04	0.03	20	10.5	0.75	0.75

304 stainless steel wire product specifications are diverse, including different wire diameters, tolerance, maximum deviation, etc., the specific specifications can be customized according to customer needs.

Hot Tags: China,custom , 304 SAE AMS 5513H-2004 Stainless steel wire manufacturer , manufacturer,factory,supplier